Corrosion protection of AZ31 magnesium alloy treated with La3+ modified 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0) conversion film
-
Add time:07/14/2019 Source:sciencedirect.com
This study demonstrated the influence of addition concentration of La3+ on the anti-corrosion behavior of a 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0) (MPS) film formed on AZ31 magnesium alloy. The morphology and surface chemistry of the samples were evaluated through scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FT-IR), respectively. The corrosion resistance of the pre-treated AZ31 magnesium alloy was studied during immersion in 0.1 mol/L NaCl solution, using potentiodynamic polarization curves and electrochemical impedance spectra (EIS). In comparison to MPS film, the low concentration of La3+ ion modified silane layer exhibited a better anti-corrosion performance, nevertheless, the high concentration of La3+ ion modified was worse. Results showed that the preferable addition concentration of La3+ ion in the silane film was 5×10−4 mol/L in this experiment.
We also recommend Trading Suppliers and Manufacturers of 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0). Pls Click Website Link as below: cas 2530-85-0 suppliers
Prev:Surface modification of oxidic nanoparticles using 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0)
Next:Study of the film formation and mechanical properties of the latexes obtained by miniemulsion co-polymerization of butyl acrylate, methyl acrylate and 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0)) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Effect of drying time of 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0) on the shear bond strength of a composite resin to silica-coated base/noble alloys07/21/2019
- Surface modification of ultrafine precipitated silica with 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0) in carbonization process07/19/2019
- Control of the electrical conductivity of composites of antimony doped tin oxide (ATO) nanoparticles and acrylate by grafting of 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0) (MPS)07/18/2019
- The effect of a 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0) and vinyltriisopropoxysilane blend and tris(3-trimethoxysilylpropyl)isocyanurate on the shear bond strength of composite resin to titanium metal07/17/2019
- Chain dynamics and stability of the poly(3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0)-co-vinylimidazole)07/16/2019
- Study of the film formation and mechanical properties of the latexes obtained by miniemulsion co-polymerization of butyl acrylate, methyl acrylate and 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0)07/15/2019
- Surface modification of oxidic nanoparticles using 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0)07/13/2019
- Preparation of silica-poly(2-hydroxyethyl methacrylate) hybrids modified with 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0)07/12/2019
- Comparative effects of untreated and 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0) treated ZnO nanoparticle reinforcement on properties of polylactide-based nanocomposite films07/11/2019