Control of the electrical conductivity of composites of antimony doped tin oxide (ATO) nanoparticles and acrylate by grafting of 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0) (MPS)
-
Add time:07/18/2019 Source:sciencedirect.com
The effect of the addition of antimony doped tin oxide (ATO) nanoparticles on the electrical conductivity of acrylate films is described. To enable dispersing of ATO in acrylate matrices, 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0) (MPS) was grafted on the surface of the filler. The amount of MPS used for this surface modification was found to strongly affect the electrical conductivity. Surface modification with a large amount of MPS resulted in colloidally stable dispersions of ATO, leading to a homogeneous distribution. Surface modification with small amounts of MPS led to instable ATO dispersions and aggregation of ATO into a fractal type network, which gives a much higher conductivity especially at low-volume fractions. For composites with a fractal type ATO network a second effect was found. Decreasing the amount of on ATO grafted MPS resulted in an increase of the electrical conduction between the ATO particles.
We also recommend Trading Suppliers and Manufacturers of 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0). Pls Click Website Link as below: cas 2530-85-0 suppliers
Prev:The effect of a 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0) and vinyltriisopropoxysilane blend and tris(3-trimethoxysilylpropyl)isocyanurate on the shear bond strength of composite resin to titanium metal
Next:Surface modification of ultrafine precipitated silica with 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0) in carbonization process) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Effect of drying time of 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0) on the shear bond strength of a composite resin to silica-coated base/noble alloys07/21/2019
- Surface modification of ultrafine precipitated silica with 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0) in carbonization process07/19/2019
- The effect of a 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0) and vinyltriisopropoxysilane blend and tris(3-trimethoxysilylpropyl)isocyanurate on the shear bond strength of composite resin to titanium metal07/17/2019
- Chain dynamics and stability of the poly(3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0)-co-vinylimidazole)07/16/2019
- Study of the film formation and mechanical properties of the latexes obtained by miniemulsion co-polymerization of butyl acrylate, methyl acrylate and 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0)07/15/2019
- Corrosion protection of AZ31 magnesium alloy treated with La3+ modified 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0) conversion film07/14/2019
- Surface modification of oxidic nanoparticles using 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0)07/13/2019
- Preparation of silica-poly(2-hydroxyethyl methacrylate) hybrids modified with 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0)07/12/2019
- Comparative effects of untreated and 3-Methacryloxypropyltrimethoxysilane (cas 2530-85-0) treated ZnO nanoparticle reinforcement on properties of polylactide-based nanocomposite films07/11/2019