Structure and properties of Lead silicate (cas 11120-22-2) glasses and melts

Add time:07/19/2019    Source:sciencedirect.com

Viscosity, density and glass transition temperature measurements were performed on the simple PbO-SiO2 system with increasing PbO content from 5 to 70 mol%. The results of these analyses have been complemented by spectroscopic studies (Raman & X-ray Absorption Spectroscopy) in order to link macroscopic properties to structural information at short- and middle-range order. A strong decrease of the viscosity is observed even with the incorporation of 5 mol% PbO, and this decrease goes on with the increase of PbO content. This effect is confirmed by the continuous decrease of the glass transition temperature with increasing PbO content. Based on our interpretations of Raman spectra, which show similarities to alkali or earth-alkaline-silicate glasses, these effects appear to arise from depolymerization of the silica network. Consequently, lead acts as a network modifier even at low content. Although, it could form PbO4 tetrahedra when it is present in large quantities, it cannot be asserted that lead acts as a network former at high lead content.

We also recommend Trading Suppliers and Manufacturers of Lead silicate (cas 11120-22-2). Pls Click Website Link as below: cas 11120-22-2 suppliers

Prev:Positron annihilation spectroscopy and third harmonic generation studies on MnO mixed lead zirconium silicate glass ceramics
Next:An efficient 2.0 μm emission of Er3+/Ho3+ co-doped Lead silicate (cas 11120-22-2) glass)