The effect of manganese additions on the high temperature oxidation behaviour of the high-vanadium cast iron

Add time:07/19/2019    Source:sciencedirect.com

Manganese (Mn) addition was found to remarkably relieve the weight gain of the wear-resistant high vanadium cast iron during oxidation at 950 °C. The mechanism of such oxidation behaviour in the associated cast iron was investigated through adding different Mn contents. During oxidation process, the decrease in weight gain was sensitive to Mn addition, where the smallest weight gain corresponded to an optimal content of 3.0 wt.% Mn. Meanwhile, the degree of macrocracks was closely dependent on Mn contents. Using FIB-TEM site-specific sample preparation technique, an initial Cr2O3 layer with a thickness of 50–200 nm was identified between the matrix cast iron and the post layer of other oxidation products. In addition, Mn additions promoted to refine the precipitating V4C3 particles that uniformly distributed in the matrix cast iron. The relationship between Mn and cracking was then analysed subsequently. Based on oxidation tests and microstructural characterization, the kinetic mechanism of oxidation behaviour of the high-vanadium cast iron at high temperature was then proposed.

We also recommend Trading Suppliers and Manufacturers of manganese vanadium oxide (cas 14986-95-9). Pls Click Website Link as below: cas 14986-95-9 suppliers

Prev:An efficient utilization of high chromium vanadium slag: Extraction of vanadium based on manganese carbonate roasting and detoxification processing of chromium-containing tailings
Next:Hydrothermal vanadium manganese oxides: Anode and cathode materials for lithium-ion batteries)