Structure and phase formation behavior and dielectric and magnetic properties of lead iron tantalate-lead zirconate titanate multiferroic ceramics

Add time:08/02/2019    Source:sciencedirect.com

Multiferroic (1 − x)Pb(Fe0.5Ta0.5)O3–xPb(Zr0.53Ti0.47)O3 (or PFT–PZT) ceramics were synthesized by solid-state reaction method. The crystal structure and phase formation of the ceramics were examined by X-ray diffraction (XRD). The local structure surrounding Fe and Ti absorbing atoms was investigated by synchrotron X-ray Absorption Near-Edge Structure (XANES) measurement. Dielectric properties were studied as a function of frequency and temperature using a LCR meter. A vibrating sample magnetometer (VSM) was used to determine the magnetic hysteresis loops. XRD study indicated that the crystal structure of the sample changed from pure cubic to mixed cubic and tetragonal with increasing PZT content. XANES measurements showed that the local structure surrounding Fe and Ti ions was similar. Dielectric study showed that the samples underwent a typical relaxor ferroelectric behavior while the magnetic properties showed very interesting behavior with square saturated magnetic hysteresis loops.

We also recommend Trading Suppliers and Manufacturers of LEAD TANTALATE (cas 12065-68-8). Pls Click Website Link as below: cas 12065-68-8 suppliers

Prev:Diffuse phase transition of Fe doped lead ytterbium tantalate ceramics
Next:The effect of zirconia substitution on the high-temperature transformation of the monoclinic-prime phase in yttrium tantalate)