Conductivity and NMR study of composite solid electrolytes based on lithium perchlorate

Add time:08/08/2019    Source:sciencedirect.com

Composite solid electrolytes 0.5LiClO4–0.5A with additives of nanocrystalline oxides A = α-Al2O3 γ-Al2O3, α-LiAlO2, γ-LiAlO2, were investigated by electrical measurements and 7Li MNR spectroscopy. It was found that composites containing γ-Al2O3 and γ-LiAlO2 have close conductivity parameters (absolute values of conductivity, σ, and activation energy, Ea); similar situation is observed in composites containing α-phases of Al2O3 and LiAlO2. Comparison shows that at the same specific surface area of the additive the composites containing γ-phases have lower Ea values and higher conductivities than ones containing α-phases. The effect is suggested to be caused by the presence of tetrahedrally-coordinated aluminum cations in the structure of γ-phases leading to the enhancement of their surface activity. Analysis of the temperature dependence of the second moment of 7Li NMR spectra shows that at temperature higher than 400K the concentration of mobile lithium ions is comparable with the total content of LiClO4 in the composites.

We also recommend Trading Suppliers and Manufacturers of Lithium perchlorate trihydrate (cas 13453-78-6). Pls Click Website Link as below: cas 13453-78-6 suppliers

Prev:Enthalpies of solution and partial molar volumes of magnesium perchlorate in alcohols and salt effect of acceleration of the Diels–Alder reaction
Next:The influence of some transition and inner transition metal oxides on the thermal decomposition of molten lithium perchlorate)