Original ArticleEvaporation-condensation derived Silicon carbide (cas 107992-37-0) membrane from Silicon carbide (cas 107992-37-0) particles with different sizes

Add time:08/20/2019    Source:sciencedirect.com

Silicon carbide (cas 107992-37-0) ceramic is a promising membrane material because of the high corrosive and high temperature resistance, and the excellent hydrophility. Here, a silicon carbide ceramic membrane with both substrate layer and separate layer composed of pure silicon carbide phase was successfully prepared. The effect of particle size on the microstructure and properties was investigated. The substrates were prepared from three silicon carbide particles at 2200 ℃. With the content increase of fine particle, the average pore size increased from 5.6 μm to 14.1 μm; meanwhile, the flexural strength of the substrate increased from 14.1 MPa to 24.6 MPa. The separation layers were made from particles of 3.0 μm and 0.5 μm. When sintered at 1900 ℃, the separation layer formed pore network with homogeneous structure. Such silicon ceramic membrane can be used in harsh conditions, including high temperature wastewater and strongly corrosive wastewater.

We also recommend Trading Suppliers and Manufacturers of Silicon carbide (cas 107992-37-0). Pls Click Website Link as below: cas 107992-37-0 suppliers

Prev:Fibronectin is a non-viral substrate for the HIV proteinase
Next:Synthesis and properties of diamond - Silicon carbide (cas 107992-37-0) composite layers)