UV-tunable upper critical solution temperature behavior of azobenzene containing poly(methyl methacrylate) in aqueous ethanol

Add time:09/25/2019    Source:sciencedirect.com

A series of azobenzene containing copolymers were synthesized by post-modification of poly(methyl methacrylate-co-pentafluorophenyl methacrylate) with an amine-functionalized azobenzene. Light- and thermo-responsive behavior of these copolymers was investigated in ethanol–water solvent mixtures with various amounts of ethanol. The upper critical solution temperature (UCST) of the polymer solutions, resulting from the poly(methyl methacrylate), was found to be highly tunable by the substitution degree of the copolymers as well as the ethanol content of the solvent mixture. In addition, the copolymers are light responsive based on the cis–trans isomerization of the azobenzene group under UV irradiation. The cloud point temperatures (TCP) of the polymer solutions decreased after UV-irradiation due to the higher dipole moment of the cis-isomer of the azobenzene moiety leading to better solubility in ethanol–water solvent mixtures. Furthermore, the UV responsiveness was found to strongly depend on the solvent composition, revealing a higher decrease in cloud point after UV-irradiation in ethanol–water solvent mixture with higher water content. To the best of our knowledge, this is the first reported dual responsive polymer that combines light responsiveness with UCST behavior in aqueous solvent mixtures.

We also recommend Trading Suppliers and Manufacturers of PENTAFLUOROPHENYL METHACRYLATE (cas 13642-97-2). Pls Click Website Link as below: cas 13642-97-2 suppliers

Prev:Synthesis and characterization of photoactive porphyrin and poly(2-hydroxyethyl methacrylate) based materials with bactericidal properties
Next:Synthesis of pentafluorophenyl(meth)acrylate polymers: New precursor polymers for the synthesis of multifunctional materials)