Kinetics of CO Oxidation by O2 or NO on Rh(111) and Rh(100) Single Crystals

Article abstract of DOI:10.1021/j100317a038

The oxidation of CO by O2 or NO over Rh(111) and Rh(100) single crystals has been studied in a high-pressure reaction-high-vacuum surface analysis apparatus.Steady-state catalytic activity as a function of temperature and partial pressures of CO, O2, and NO has been measured.The CO-O2 reaction was found to be insensitive to the structure of the surface as evidenced by the identical rates, activation energies, and partial pressure dependencies measured on the two single-crystal surfaces.Both surfaces deactivated at high O2 partial pressures due to the formation of a near-surface oxide (probably Rh2O3) which is catalytically inactive for this reaction.The deactivation occured at a slightly lower O2 partial pressure on Rh(100), likely due to the relative ease of oxygen diffusion through this surface leading to more rapid bulk oxidation.Unlike the CO-O2 reaction, CO oxidation by NO was very sensitive to the geometric structure of the surface.This behavior was evident in all kinetic parameters measured on the two surfaces.The kinetic data obtained on Rh(111) agree quantitatively with a surface chemistry model previously developed for this reaction.The model predicts that the rate is limited by the formation of N2 from the recombination of adsorbed N atoms, and that the surface, under steady-state reaction conditions, is covered largely with adsorbed N atoms and smaller amounts of adsorbed NO.On Rh(100) the data are consistent with a reaction rate limited by the formation of N2 from the surface reaction of adsorbed NO and N atoms.